fatigue and corrosion fatigue behaviors of g105 and s135 suppliers, distributors, production and supply of fatigue and corrosion fatigue behaviors of g105 and s135, are committed to providing high-quality products, as well as excellent cutting, forming, drilling and other processing services. If you have any needs, please feel free to contact:

[email protected]


Fatigue and corrosion fatigue behaviors of G105 and S135

Fatigue and corrosion fatigue (CF) tests were carried out to investigate the behaviors of G105 and S135 low carbon highstrength drill pipe steels under different stress amplitudes in air as Characteristics and life eion of fatigue fracture of Oct 01, 2020 · The fatigue limits are 0.484, 0.514 for G105, S135 steels at R = 0.1 and 0.517 for S135 steel at R = 1, respectively. (3) The fatigue strength coefficient can be estimated by the theoretical cohesive strength of the steel, which depends on Youngs modulus or fracture properties from the tensile test. Characteristics and life eion of fatigue fracture of Fatigue and corrosion fatigue (CF) tests were carried out to investigate the behaviors of G105 and S135 low carbon highstrength drill pipe steels under different stress amplitudes in air as Sulfide Stress Corrosion Cracking Behavior of G105 and Feb 13, 2019 · Slow strain rate testing was employed to investigate the sulfide stress corrosion cracking (SSCC) behavior of low-carbon high-strength drill pipe steels (G105 and S135) in the simulated drilling environment containing H 2 S. Results reveal that both G105 and S135 steels have a high SSCC susceptibility in the simulated drilling environment containing H 2 S. Experimental and theoretical study on the mechanical Aug 17, 2021 · Han L, Liu M, Luo S et al (2019) Fatigue and corrosion fatigue behaviors of G105 and S135 highstrength drill pipe steels in air and H2S environment. Process Saf Environ Prot 124:6374. Article Google Scholar 26. Analysis of fatigue behaviour of drill pipe on pin-box Aug 27, 2020 · Fatigue and corrosion fatigue behaviors of G105 and S135 high strength drill pipe steels in air and H2S environment. Process Saf Environ Protect 2019 ; 124:63 74 . Google Scholar Crossref Reliability Prediction of Variable Amplitude Corrosion [2] Lihong Han, Ming Liu,Sheji Luo, et al,Fatigue and corrosion fatigue behaviors of G105 and S135 high-strength drill pipe steels in air and H2S environment, Process Safety and Environmental Protection 124 (2019)63-74. DOI:10.1016/j.psep.2019.01.023 Ming Liu - TU DelftFatigue and corrosion fatigue behavior of G105 and S135 high-strength drill pipe steels in air and H 2 S environment. Process Safety and Environmental Protection , 2019, 124:63-74. [3] Ming Liu, Xuequn Cheng, Xiaogang Li, Cheng Zhou, Helin Tan. Optimization of the Structural Parameters and the Teeth May 07, 2021 · May 07, 2021 · L. Han, M. Liu, S. Luo, and T. J. Lu, Fatigue and corrosion fatigue behaviors of G105 and S135 high-strength drill pipe steels in air and H 2 S environment, Process Safety and Environmental Protection, vol. 124, no. 4, pp. 6374, 2019. View at:Publisher Site Google Scholar

Contact us